Yottha Srithep1,*, Onpreeya Veang-in1, Dutchanee Pholharn2, Lih-Sheng Turng3, John Morris4
Journal of Renewable Materials, Vol.9, No.7, pp. 1267-1281, 2021, DOI:10.32604/jrm.2021.015604
- 18 March 2021
Abstract A low-molecular-weight polylactide-poly(butylene succinate) (PLA-PBS) copolymer was synthesized and incorporated into polylactide (PLA) as a novel toughening agent by solvent casting. The copolymer had the same chemical structure and function as PLA and it was used as a plasticizer to PLA. The copolymer was blended with PLA at a weight ratio from 2 to 10 wt%. Phase separation between PLA and PLA-PBS was not observed from their scanning electron microscopy (SEM) images and the crystal structure of PLA almost remained unchanged based on the X-ray diffraction (XRD) measurement. The melt flow index (MFI) of the… More >