Yu Wang^1,2, Mengyang Ma^1,2,*, Yong Long^1,2, Qingxiang Zhao^1,2, Zhifei Cheng^1,2

FDMP-Fluid Dynamics & Materials Processing, Vol.20, No.8, pp. 1773-1784, 2024, DOI:10.32604/fdmp.2024.048695 - 06 August 2024

Abstract Shrinkage-induced cracking is a common issue in concrete structures, where the formation of cracks not only affects the aesthetic appearance of concrete but also potentially reduces its durability and strength. In this study, the effect of ceramsite sand addition on the properties of a ternary system of cement-ground granulated blast furnace slag (GGBFS)-phosphogypsum (PG) is investigated. In particular, the fluidity, rheology, hydration heat, compressive strength, autogenous shrinkage, and drying shrinkage of the considered mortar specimens are analyzed. The results indicate that an increase in PG content leads to a decrease in fluidity, higher viscosity, lower More >

Haodong Li¹, Huiling Du^1,*, Le Kang¹, Yewen Zhang¹, Tong Lu¹, Yuchan Zhang¹, Lan Yang², Shijie Song²

Journal of Renewable Materials, Vol.11, No.12, pp. 4161-4174, 2023, DOI:10.32604/jrm.2023.028877 - 10 November 2023

Abstract The large accumulation of coal gangue, a common industrial solid waste, causes severe environmental problems, and green development strategies are required to transform this waste into high-value-added products. In this study, low-cost ceramsites adsorbents were prepared from waste gangue, silt coal, and peanut shells and applied to remove the organic dye methylene blue from wastewater. We investigated the microstructure of ceramsites and the effects of the sintering atmosphere, sintering temperature, and solution pH on their adsorption performance. The ceramsites sintered at 800°C under a nitrogen atmosphere exhibited the largest three-dimensional-interconnected hierarchical porous structure among the… More > Graphic Abstract

Suiwei Pan¹, Anqi Ren¹, Yongli Peng¹, Min Wu², Wanguo Dong³, Chunlin Liu², Depeng Chen^2,*

Journal of Renewable Materials, Vol.11, No.2, pp. 881-904, 2023, DOI:10.32604/jrm.2022.023000 - 22 September 2022

Abstract This study focuses on the workability and compressive strength of ceramsite self-compacting concrete with fine aggregate partially substituted by steel slag sand (CSLSCC) to prevent the pollution of steel slag in the environment. The SF, J-ring, visual stability index, and sieve analysis tests are primarily employed in this research to investigate the workability of freshly mixed self-compacting concrete containing steel slag at various steel slag sand replacement rates. The experiment results indicate that CSLSCC with the 20% volume percentage of steel slag (VPS) performs better workability, higher strength, and higher specific strength. The 7-day compressive More > Graphic Abstract

Lei Tian, Liuchao Qiu^*, Jingjun Li, Yongsen Yang

Journal of Renewable Materials, Vol.8, No.2, pp. 154-170, 2020, DOI:10.32604/jrm.2020.08701 - 01 February 2020

Abstract In recent decades, the utilization of waste tires, plastic and artificial shale ceramsite as alternative fine aggregate to make self-compacting concrete (SCC) has been recognized as an eco-friendly and sustainable method to manufacture renewable construction materials. In this study, three kinds of recycled aggregates: recycled tire rubber particles, wood-plastic particles, artificial shale ceramsite were used to replace the sand by different volume (5%, 10%, 20% and 30%), and their effects on the fresh and hardened properties of SCC were investigated. The slump flow and V-funnel tests were conducted to evaluate the fresh properties of modified-SCC… More >