Jaewook Lee¹, Byung-Dae Park^1,*, Qinglin Wu²

Journal of Renewable Materials, Vol.12, No.7, pp. 1187-1205, 2024, DOI:10.32604/jrm.2024.049948 - 21 August 2024

Abstract Lignin is the most abundant aromatic natural polymer, and receiving great attention in replacing various petroleum-based polymers. The aim of this study is to investigate the feasibility of technical lignin as a polyol for the synthesis of non-isocyanate polyurethane (NIPU) adhesives to substitute current polyurethane (PU) adhesives that have been synthesized with toxic isocyanate and polyols. Crude hardwood kraft lignin (C-HKL) was extracted from black liquor from a pulp mill followed by acetone fractionation to obtain acetone soluble-HKL (AS-HKL). Then, C-HKL, AS-HKL, and softwood sodium lignosulfonate (LS) were used for the synthesis of technical lignin-based… More > Graphic Abstract

Louis C. Muller^1*, Sanette Marx¹, Hermanus C.M. Vosloo²

Journal of Renewable Materials, Vol.5, No.1, pp. 67-80, 2017, DOI:10.7569/JRM.2016.634130

Abstract This work reports a study of polyol synthesis through liquefaction of technical lignins in crude glycerol by means of 1H and 31P NMR spectroscopy. The polyols are intended for preparation of polyurethane foam; thus, it is important to know how different lignin types as well as crude glycerol influence and contribute to the final polyol hydroxyl contents. Polyols prepared from organosolv lignin, kraft lignin and lignosulphonate had hydroxyl numbers suitable for rigid foam of 435, 515 and 529 mgKOH/g, respectively. The polyols differed in composition with glycerol, showing significant variation. During liquefaction the glycerol content More >