C. Colombo1, M. Guagliano1,2, L. Vergani1
Structural Durability & Health Monitoring, Vol.1, No.4, pp. 253-266, 2005, DOI:10.3970/sdhm.2005.001.253
Abstract In this paper the fatigue crack growth properties of a nitrided and shot-peened steel is dealt with: different peening intensities were considered and the resulting residual stresses measured by means of an X-ray diffractometer. Rotating bending fatigue tests were executed on specimens including a blind micro hole, acting as a pre-existent crack. The fracture surface of broken specimens was observed with a SEM to detect the crack growth initiation point. The run-out specimens were broken after the test and the presence of non-propagating cracks detected. The results allowed to determine the propagation threshold of the More >