Zhengfan Lyu^1,3, Yulin Li^2,3, Mengmeng Fan^1,3,*, Yan Huang¹, Chenguang Li²

FDMP-Fluid Dynamics & Materials Processing, Vol.20, No.5, pp. 901-913, 2024, DOI:10.32604/fdmp.2023.043512 - 07 June 2024

Abstract Red mud (RM) is a low-activity industrial solid waste, and its utilization as a resource is currently a hot topic. In this study, the micro characteristics of red mud at different calcination temperatures were analyzed using X-ray diffraction and scanning electron microscopy. The performance of calcined red mud was determined through mortar strength tests. Results indicate that high-temperature calcination can change the mineral composition and microstructure of red mud, and increase the surface roughness and specific surface area. At the optimal temperature of 700°C, the addition of calcined red mud still leads to a decrease More > Graphic Abstract

Cheng Hu^1,2, Weiheng Xiang^1,3,*, Ping Chen^2,3, Yi Yang^4,5, Libo Zhou³, Jiufang Jiang⁵, Shunkai Li^2,4, Yang Ming¹, Qing Li³

Journal of Renewable Materials, Vol.11, No.11, pp. 3945-3956, 2023, DOI:10.32604/jrm.2023.027544 - 31 October 2023

Abstract The aim of this study is to enhance the value and utilization of red mud generated in the Bayer process by preparing composite cement mortars. The effects of two different types of Bayer red mud with varying physical and chemical characteristics on the fluidity, mechanical strength, mineral composition, and microstructure of the composite cement mortar were systematically evaluated. The results showed that the optimal addition of red mud A was 10 wt%, while it was 20 wt% for red mud B. The mechanical properties of the composite cement mortar met the standards for P·O42.5 cement. More >

Yanrong Zhao^1,2,3,#, Ping Chen^1,4,*,#, Shifeng Wang⁵, Yaxiong Ji^3,4, Yuanhao Wang^3,4,*, Bolin Wu^1,2, Rongjin Liu¹

Journal of Renewable Materials, Vol.8, No.11, pp. 1531-1541, 2020, DOI:10.32604/jrm.2020.011462 - 28 September 2020

Abstract Bayer red mud (BRM) is a kind of industrial solid waste characterized by huge volume and high alkalinity. Its disposal generates serious environmental pollution and occupies a large number of farmland. The utilization and recycling of BRM is currently a crucial issue and needs to be addressed as soon as possible. The chemical composition of BRM is similar to cement clinker. In this study, the feasibility of preparing Belite-ferroaluminate clinker (BFAC) with different BRM was explored. The physical properties, mechanics performance, radioactivity levels and trace harmful metals leaching were measured. XRD, BEI and EDS were… More >