Journal of Renewable Materials, Vol.11, No.6, pp. 2695-2712, 2023, DOI:10.32604/jrm.2023.025711 - 27 April 2023

Abstract The destruction of recombinant bamboo depends on many factors, and the complex ambient temperature is an important factor affecting its basic mechanical properties. To investigate the failure mechanism and stress–strain relationship of recombinant bamboo at different temperatures, eighteen tensile specimens of recombinant bamboo were tested. The results showed that with increasing ambient temperature, the typical failure modes of recombinant bamboo were flush fracture, toothed failure, and serrated failure. The ultimate tensile strength, ultimate strain and elastic modulus of recombinant bamboo decreased with increasing temperature, and the ultimate tensile stress decreased from 154.07 to 96.55 MPa, a decrease More > Graphic Abstract

Yang Wei^*, Kunpeng Zhao, Chen Hang, Si Chen, Mingmin Ding

Journal of Renewable Materials, Vol.8, No.3, pp. 251-273, 2020, DOI:10.32604/jrm.2020.08779 - 01 March 2020

Abstract The creep behavior of bamboo due to the complicated influences of environment and stress will lead to a sustained increase in deformation, which serious effects the service performance of structures. To investigate the creep behavior of recombinant bamboo, twenty-four recombinant bamboo specimens were tested under lasting compressive and tensile loads at different load levels. The typical failure modes of recombinant bamboo under a lasting load at a high load level were buckling failure and brittle fracturing due to creep compressive creep and tensile creep development, respectively. At a high load level, the creep deformation of… More >