Tezara Cionita^1,*, Mohammad Hazim Mohamad Hamdan², Januar Parlaungan Siregar^3,4,*, Deni Fajar Fitriyana⁵, Ramli Junid⁶, Wong Ling Shing⁷, Jamiluddin Jaafar⁸, Agustinus Purna Irawan⁹, Teuku Rihayat¹⁰, Rifky Ismail¹¹, Athanasius Priharyoto Bayuseno¹¹, Emilianus Jehadus¹²

Journal of Renewable Materials, Vol.12, No.3, pp. 457-483, 2024, DOI:10.32604/jrm.2024.045814 - 11 April 2024

Abstract Recent decades have seen a substantial increase in interest in research on natural fibres that is aligned with sustainable development goals (SDGs). Due to their renewable resources and biodegradability, natural fiber-reinforced composites have been investigated as a sustainable alternative to synthetic materials to reduce the usage of hazardous waste and environmental pollution. Among the natural fibre, jute fibre obtained from a bast plant has an increasing trend in the application, especially as a reinforcement material. Numerous research works have been performed on jute fibre with regard to reinforced thermoset and thermoplastic composites. Nevertheless, current demands More >

S. ARULMURUGAN^a,*, N. VENKATESHWARAN^a, S. KUMAR^a, P. CHANDRASEKAR^a

Journal of Polymer Materials, Vol.40, No.1-2, pp. 83-91, 2023, DOI:10.32381/JPM.2023.40.1-2.7

Abstract In this research, the effect of UV light on the mechanical properties of jute polymer nanocomposites was evaluated. Due to the fact that photodegradation is a surface process and is confined to the degradation of the mechanical characteristics of polyester resin, this study focuses on the resin quality. Therefore, test samples comprised of fibre-reinforced polyester nanoclay composites were fabricated different weight ratios of nanoclay. They were put through UV exposure in an Ultraviolet (UV) chamber. Tensile testing samples were made in accordance with ASTMD638 and had a minimum thickness of 3 mm. Additionally, specimens for… More >

M. VASUMATHI^1,a,*, VELA MURALI^2,b, S. RASHIA BEGUM^1,c, N. RAJENDRAN^2,d

Journal of Polymer Materials, Vol.36, No.1, pp. 1-11, 2019, DOI:10.32381/JPM.2019.36.01.1

Abstract In the Fibre Metal Laminate (FML), Carbon Reinforced Aluminium laminate (CARALL), aluminium is placed next to carbon fibres. The potential difference between the aluminium and carbon is larger, leads to galvanic corrosion, which tries to bring down the durability of the FML. To bring down the effect of corrosion, a material layer is introduced between fibres and aluminium so as to separate them thus lowering the possibility of occurrence of corrosion. Another approach is to coat the surfaces of aluminium with different proportions of aluminium oxide nano particles prior to fabrication of the FML. For More >