Selwin Maria Sekar¹, Rajini Nagarajan^1,*, Ponsuriyaprakash Selvakumar², Ismail Sikiru Oluwarotimi³, Kumar Krishnan⁴, Faruq Mohammad⁵, Mohammed Rafi Shaik⁵, Nadir Ayrilmis^6,*

Journal of Renewable Materials, Vol.12, No.8, pp. 1455-1474, 2024, DOI:10.32604/jrm.2024.052952

Abstract An innovative microcrystalline cellulose (MCC) natural fibre powder-reinforced PLA biocomposite was investigated using the hand lay-up technique. The polymer matrix composite (PMC) samples were prepared by varying the weight percentages (wt.%) of both PLA matrix and MCC reinforcement: pure PLA/100:0, 90:10, 80:20, 70:30, 60:40 and 50:50 wt.%, respectively. From the results obtained, MCC powder, with its impressive aspect ratio, proved to be an ideal reinforcement for the PLA, exhibiting exceptional mechanical properties. It was evident that the 80:20 wt.% biocomposite sample exhibited the maximum improvement in the tensile, flexural, notched impact, compressive strength and hardness… More >

HADIMANI SHIVAKUMAR¹, GURUMURTHY G. D.¹, BOMMEGOWDA K. B.², S. PARAMESHWARA³

Journal of Polymer Materials, Vol.40, No.1-2, pp. 93-103, 2023, DOI:10.32381/JPM.2023.40.1-2.8

Abstract Polymer composites are increasing in demand in energy storage applications including in the electronic as well as electrical industries due to the ease of processing of these materials with associated advantages like light weight, corrosion resistance, and high mechanical strength. In this investigation, efforts are made to enhance the charging and discharging properties of epoxy/carbon fabric composite by the addition of graphene nanoplatelets (GNPs) into the epoxy/ carbon matrix. The performance of the composites with graphene platelets of 0.5 to 5 wt. % in epoxy were characterized and 1wt.% percolation threshold was observed poor performance… More >