Evaluation of Novel Chitosan Based Composites Coating on Wettability for Pure Titanium Implants

by Qahtan A. Hamad¹, Hanaa A. Al-Kaisy¹, Mohanad N. Al-Shroofy¹, Noor K. Faheed^2,*

1 Materials Engineering Department, University of Technology, Baghdad, Iraq
2 Petroleum Engineering Department, University of Misan, Amara, Iraq

* Corresponding Author: Noor K. Faheed. Email:

(This article belongs to the Special Issue: Bio-based Composite/Hybrid Structures and Components)

Journal of Renewable Materials 2023, 11(4), 1601-1612. https://doi.org/10.32604/jrm.2023.023213

Received 14 April 2022; Accepted 10 June 2022; Issue published 01 December 2022

Abstract

This work aims to prepare chitosan (CS)-based coated layers, CS (10 wt% nanosilver/90 wt% CS, 10 wt% biotin/90 wt% CS, and 5 wt% nanosilver–5 wt% biotin)/90 wt% CS coatings are prepared, onto pure Ti substrate. The surface morphology of the novel CS composite coating was studied using field emission scanning electron microscopy, atomic force microscopy (AFM), Fourier transforms infrared (FTIR) and wettability test. Results show that the addition of (biotin, nanosilver) 5 Vol.% improves the properties of composite materials. Using different particles’ scale size aid in improving the combinations in the alginate, producing a dual effect on film properties. Coating surface roughness decreased in the chitosan-based biocomposite with preferable homogeneity and crack-free coating layers, as confirmed by AFM. An increase in surface roughness ensured substitution, which enhanced the surface structures. The high wettability of the CS-based coating layers was due to the presence of nanoparticles, and the composite coatings with CS, nanosilver, or biotin had excellent wettability because of the good hydrophilic nature of the CS matrix combined with reinforced particles. The FTIR results showed that peaks of the blending of CS plus nanoparticles, CS plus biotin, or CS plus nanosilver plus biotin were excellent matching with no changes in the structure of the matrix.

---