A Melamine–Dialdehyde Starch Wood Particleboard Surface Finish without Formaldehyde

by Bengang Zhang^1,*, Antonio Pizzi^2,*, Mathieu Petrissans¹, Anelie Petrissans¹, Baptiste Colin¹

1 LERMAB, I.U.T. Hubert Curien, University of Lorraine, Épinal, 88000, France
2 LERMAB-ENSTIB, University of Lorraine, Épinal, 88000, France

* Corresponding Authors: Antonio Pizzi. Email: ; Bengang Zhang. Email:

Journal of Renewable Materials 2023, 11(11), 3867-3889. https://doi.org/10.32604/jrm.2023.028888

Received 13 January 2023; Accepted 10 February 2023; Issue published 31 October 2023

Abstract

Melamine-dialdehyde starch resins used for wood surface finishes have been developed. The reaction of melamine with dialdehyde starch has been shown to occur by FTIR and MALDI ToF spectrometry, with several oligomer species due to the reaction of the two materials being identified, and the resin thermal stability was studied by thermogravimetric analysis. The resins were prepared by two different procedures when it was realized that dialdehyde starch is sensitive to too high a temperature for prolonged times. The melamine-dialdehyde starch resins were applied on particleboard supports as a direct liquid surface finish and a resin-impregnated paper. The surface finishes were tested for adhesion by the cross-cut test, their initial sessile drop contact angle, and the contact angle evolution as a function of time. The best results were obtained by the resins catalyzed by 2% ammonium sulfate and applied to the support surface as a resin-impregnated paper hot pressed for 3 min at 200°C, although the results at 180°C also looked promising.

---

Keywords

---