The Antibacterial Activities of Copper Oxide Nanoparticles Synthesized Using Laser Ablation in Different Surfactants against Streptococcus mutans

Ruaa H. Abbas1, A. Kadhim1,*, Azhar M. Haleem2

1 Laser and Optoelectronics Engineering Department, University of Technology-Iraq, Baghdad, Iraq
2 Environmental Research Center, University of Technology-Iraq, Baghdad, Iraq

* Corresponding Author: A. Kadhim. Email: email

(This article belongs to this Special Issue: New Insights on Nanomaterials for Energy, Environmental and Agricultural Applications)

Journal of Renewable Materials 2023, 11(5), 2109-2123. https://doi.org/10.32604/jrm.2023.025112

Abstract

Copper oxide nanoparticles (CuO NPs) were synthesised with laser ablation of a copper sheet immersed in deionized water (DW), cetrimonium bromide (CTAB), and sodium dodecyl sulphate (SDS), respectively. The target was irradiated with a pulsed Nd: YAG laser at 1064 nm, 600 mJ, a pulse duration of 10 ns, and a repetition rate of 5 Hz. The CuO NPs colloidal were analyzed using UV–Vis spectroscopy, the Fourier transform infrared (FTIR) spectrometer, zeta potential (ZP), X-ray diffraction (XRD), transmission electron microscope (TEM) and field emission scanning electron microscopy (FESEM). The absorption spectra of CuO NPs colloidal showed peaks at 214, 215 and 220 nm and low-intensity peaks at 645, 650 and 680 nm for SDS, CTAB and DW, respectively. CuO NPs’ colloidal results are (−21.6, 1.2, and 80 mV) for negatively, neutrally, and positively charged SDS, DW, and CTAB, respectively. The XRD pattern of the NPs revealed the presence of CuO phase planes (110) (111), (20-2) and (11-1). The TEM images revealed nearly spherical NPs, with sizes ranging from 10–90, 10–50, and 10–210 nm for CuO NPs mixed with DW, SDS and CTAB, respectively. FESEM images of all the synthesized samples illustrate the formation of spherical nanostructure and large particles are observable. The CuO NPs were tested for antibacterial activity against Streptococcus mutans by using the well diffusion method. In this method, CuO NPs prepared in DW at a concentration of 200 μg/mL showed a greater inhibition zone against Streptococcus mutans.

Keywords


Cite This Article

Abbas, R. H., Kadhim, A., Haleem, A. M. (2023). The Antibacterial Activities of Copper Oxide Nanoparticles Synthesized Using Laser Ablation in Different Surfactants against Streptococcus mutans. Journal of Renewable Materials, 11(5), 2109–2123.



cc This work is licensed under a Creative Commons Attribution 4.0 International License , which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
  • 1358

    View

  • 588

    Download

  • 0

    Like

Share Link