TY - EJOU AU - Lin, Heng-Cheng AU - Kung, Chieh AU - Chen, Rong-Sheng AU - Liang, Gin-Tiao TI - An Optimization Analysis of UBM Thicknesses and Solder Geometry on A Wafer Level Chip Scale Package Using Robust Methods T2 - Computers, Materials \& Continua PY - 2006 VL - 3 IS - 2 SN - 1546-2226 AB - Wafer level chip scale package (WLCSP) has been recognized providing clear advantages over traditional wire-bond package in relaxing the need of underfill while offering high density of I/O interconnects. Without the underfill, the solder joint reliability becomes more critical. Adding to the reliability concerns is the safety demand trend toward "green'' products on which unleaded material, e.g. lead-free solders, is required. The requirement of lead-free solders on the packages results in a higher reflow temperature profile in the package manufacturing process, in turn, complicating the reliability issue. This paper presents an optimization study, considering the fatigue reliability, for a wafer level chip scale IC package in which a Ti/Cu/Ni UBM is involved. A finite element model is developed for the package. The model employs Sn3.8Ag0.7Cu lead-free solders built on build-up layers with micro-vias. Finite element analyses are performed to study the mechanical behaviors of the package elements in which the solder as well as the UBM is of interest. Firstly, a Surface Evolver program is used to construct the solder based non-solder mask defined (NSMD) pad. Then, multi-purpose finite element software, ANSYStm, is used to create a double symmetric 3-D numerical model to investigate the mechanical behaviors including deformation, stress-strain relation as well as hysteresis loops for temperature cycles. The Garofalo-Arrhenius Creep Model is employed. A modified Coffin-Manson formula is also employed to estimate the fatigue life for the package. Finally, the Taguchi robust analysis is adopted for optimization analysis of UBM thicknesses and solder geometry. Our results show that thicker UBM layers tend to increase the fatigue life while a small solder pad will prolong the fatigue life and as volume increases so does the fatigue life. From the results of Taguchi robust analysis, it is shown that among the factors of UBM layer thickness, solder pad radius and solder volume, the solder volume is the most dominating factor on the fatigue life of the package. The optimal combination of UBM thickness set at 0.0066 mm (level 3), solder pad radius set at 0.10 mm (Level 1), and solder volume set at 0.020 mm3 (Level 3) contributes the greatest fatigue life of 1229 cycles which is 448% gained over our reference package model. KW - Wafer level package KW - Lead-free KW - Finite element analysis KW - Robust design DO - 10.3970/cmc.2006.003.055